Lantor Soric XF

The Soric® XF grades have fast resin flow combined with optimized weight reduction. The hexagonal pattern offers a reduced resin consumption making the Soric® XF grade suitable for thicker laminates.

The cost-effective solution for closed mold processes.

Is used as core material and infusion medium.

Is a pressure stable polyester nonwoven and compatible with all regular types of resins, including polyester, vinylester, phenolic and epoxy.

Is suitable for closed mold processes, including Infusion, RTM Light, RTM Heavy.

Applications:

·         Marine: hulls, decks and structures of boats and yachts

·         Transportation: parts and panels of cars, trailers, trucks and RV’s

·         Mass transit: interior and exterior of trains, light rail and buses

·         Leisure: kayaks, surfboards, pools and tubs

·         Industrial: cladding panels, fans, containers and tanks

·         Wind Energy: nacelle and spinners

 

Dimensional Data:

Mechanical Properties

XF 1.5

XF 2

XF 3

XF 4

XF 5

XF 6

XF 10

Thickness: mm

1.5

2.0

3.0

4.0

5.0

6.0

10.0

Roll Length: m

70

80

50

40

30

25

15

Roll Width: m

1.27

1.27

1.27

1.27

1.27

1.27

1.27

Thickness loss at 0.8 bar: %

< 10

< 10

< 10

< 10

< 10

< 10

< 10

Max Processing temp.: oC

170

170

170

170

170

170

170

Resin Uptake: kg/m2

1.0

1.0

1.4

1.9

2.4

2.8

5.4

Dry Weight: g/m2

100

135

180

250

320

345

625

Density Impregnated kg/m3

650

600

600

600

600

600

600

 

Typical mechanical properties of Lantor Soric XF impregnated with unsaturated polyester resin:

Mechanical Properties

Unit

Value

Test Method

Flexural Strength

MPa

8

ASTM D790

Flexural Modulus

MPa

800

ASTM D790

Tensile Strength Across Layers

MPa

4

ASTM C297

Compression Strength: 10% strain

MPa

8

ISO 844

Shear Strength

MPa

3.5

ASTM C273-61

Shear Modulus

MPa

35

ASTM C273-61